PHILOS plate fixation with polymethyl methacrylate cement augmentation of an osteoporotic proximal humerus fracture
Article information
Abstract
PHILOS plate fixation in osteoporotic proximal humerus fracture of old age is well-known for high complication rate, especially metal failure, providing various augmentation techniques, such as calcium phosphate cement, allogenous or autologous bone graft. We report a case of polymethyl methacrylate augmentation to provide appropriate reduction with a significant mechanical support. This can be a treatment option for displaced unstable osteoporotic proximal humerus fracture with marked bony defect.
Proximal humerus fractures are common in the elderly, the second most common fracture in the upper extremity, and lead to high morbidity and loss of function [1,2]. The incidence of proximal humerus fractures in Finland was 82 per 100,000 person-years, and 73% of patients with proximal humerus fractures were women. The Incidence increased with older age groups [3]. Another study revealed that osteoporotic bone increased the risk of proximal humerus fractures and suggested that the high incidence of proximal humerus fractures in older female patients is likely to be related to osteopenia and osteoporosis [4]. Because of the various complications after fixation of a proximal humerus fracture using a plate (e.g., osteonecrosis of the humeral head, humeral head settling with loss of neck-shaft angle, nonunion or malunion, screw penetration into the glenohumeral joint, and implant failure), there has yet to be an accepted consensus on the clear surgical indication for treatment of theses fractures [5]. During surgery for a proximal humerus fracture, a surgeon sometimes encounters a metaphyseal void after reduction of impaction of the metaphysis. Several strategies exist for void filling to help structural stability, enhance healing, and minimize failure of fixation [6]. Bone cement is commonly used in orthopedic surgery due to its osteoconductive properties and resistance to compression force [7]. For example, augmentation with calcium phosphate cement in the treatment of proximal humeral fractures with locked plates increased fracture settling and significantly decreased intra-articular screw penetration in one report [6]. Herein, we present a case of polymethyl methacrylate (PMMA) cement augmentation in a failed osteoporotic proximal humerus fracture.
CASE REPORT
This study was approved by the Institutional Review Board of Hallym University Chuncheon Sacred Heart Hospital (IRB No. 2020-07-003).
A 56-year-old female was sent to our emergency department after a fall in which she landed on her left arm. The patient complained about left shoulder pain, swelling and ecchymosis. On palpation, tenderness was noted all around the shoulder, especially at the level of the axilla. Both neurological and vascular examinations were normal. Anteroposterior X-ray and computed tomography of the left shoulder showed a two-part surgical neck fracture of the proximal humerus (Fig. 1). A preoperative bone mineral density showed osteoporosis (T=–3.8).
Three days after the injury, an open reduction and internal fixation (ORIF) was performed with the Proximal Humerus Internal Locking System (PHILOS; DePuy Synthes, Raynham, MA, USA) plate and screws. On postoperative day (POD) 4, the patient fell down from her bed, and there was screw back-out and reduction loss at the humeral head (Fig. 2).
Thus, revisional ORIF was done on POD 7. Using the previous incision (deltopectoral approach), we removed the previous locking plate. After the revisional ORIF with a PHILOS plate and screws, including a long calcar screw, a metaphyseal defect developed. Thus, we put PMMA cement in the void area to fill the defect and provide structural stability (Fig. 3A, B). We applied an abductor brace. The postoperative X-ray showed firm fixation with the PHILOS plate and cement augmentation (Fig. 3C, D).
After 4 weeks of immobilization, the brace was removed, and the patient started exercise to increase the range of motion of the shoulder joint (forward elevation, 120°; external oration, 60°; internal rotation, L3 level). At that time, a follow-up X-ray showed healing of the fracture without screw backout or loss of reduction. Three months after the revision operation, the patient’s range of motion was within the normal range (forward elevation, 150°; external oration, 80°; internal rotation, T8), her pain was tempered (visual analog scale score, 1), and the function of her shoulder was improved (American Shoulder and Elbow Surgeons [ASES] score, 73.3; Korean Shoulder Scoring [KSS] system score, 82).
Finally, 6 months after the revision operation, the patient was pain-free with full range movement of the left shoulder and improved clinical outcomes (ASES score, 80.2; KSS score, 92). X-rays revealed union of the proximal humerus fracture with no sign of avascular necrosis of the humeral head (Fig. 4).
DISCUSSION
The present case demonstrated a satisfactory result from ORIF using a precontoured PHILOS plate combined with PMMA cement augmentation for an osteoporotic proximal humerus fracture. Compared to other materials, such as calcium phosphate cement, allogeneic bone or autologous bone, PMMA cement provides a reduced fracture with significant mechanical support [6-9].
Osteoporotic proximal humerus fracture has high rates of complication and reoperation. There are many augmentation techniques for fixation with a plate as follows: structural allogeneic or autologous bone grafting to enhance the medial support, filling the metaphyseal void with synthetic bone substitutes or bone grafts, and screw-tip augmentation with bone cement [6]. Some studies revealed that bone grafting to fill the void had a positive effect on healing the fracture and reducing the failure rate [8]. One review showed that PMMA augmentation of proximal femoral nail fixation might have the potential to prevent reoperations by strengthening the osteosynthesis construct [9]. In the present case, there is a possibility that some thermal injury occurred from the PMMA cement, but it was used for its ability to provide mechanical support.
Although bone graft or calcium phosphate cement might be better than PMMA cement in the aspect of biocompatibility, PMMA cement augmentation could be better for unstable fractures with severe osteoporotic bone in the aspect of mechanical support. Therefore, the present case report provides another surgical option for displaced osteoporotic proximal humerus fractures with significant bony defects: ORIF with PMMA cement augmentation. Moreover, this option may also be applied for a revisional ORIF of an osteoporotic proximal humerus fracture.